wear resistant coatings > BD40264 high temperature brushable ceramic epoxy coatings

BD40264 high temperature brushable ceramic epoxy coatings

BD40264 high temperature resistant brushable ceramic coating

Product description:
This product is high temperature resistant,wear resistant and corrosion resistant polymer material which compounded by modified high temperature toughening resin and a variety of abrasion resistant and corrosion resistant materials,it is widely used in the preparation of protective coating on the surface of various machine part which has wear resistant and corrosion resistant requirements in high temperature environment,it is suitable for the pre-protect of pump,valves,pipeline,heat exchanger end plate,blade,
tank body etc. equipment new parts,repairing and refurbishment of the above equipment after it suffers from wear and corrosion in high temperature environment.

Performance Index:

Color	Physical state	Compressive strength (Mpa) GB/1041-2008	Density (g/cm3)	Shear strength (Mpa) GB/7124-2008	tensile strength (Mpa) GB6329-2009	hardness after curing （Shore D） ASTM-D-2556
Grey	Semi-fluid	67	1.61	23	47	86

Operational time limit (25℃)	Fully curing time	Operating temperature in hot and humid environment (℃)	Operating temperature in dry environment (℃)
30 -60 min	Room temperature:24 hours,room temperature 2 hours + 80 deg C 1 hour	-40-85	-60-180

How to use:
1. Surface treatment:The pending-repair parts were treated with rust removal and coarsening, and then cleaned with cleaning agent.

2. Preparation:Make the Part A and Part B mix uniformly according to mixing weight ratio A:B = 10 :1,and use it up within the specified operational time limit.

3. Coating:Make the mixed prepared materials be coating on the pending-repair parts,for large area protection,you could do multi-layer brush coating in a Criss Cross way according to the requirements of the project,the thickness of each layer should be controlled in 0.3 to 0.5mm

4. Curing:It can be put into using after curing for 24 hours at the temperature of 25 to30 deg C,when the construction environment temperature is below 15 deg C,you should heat it up or prolong the curing time to promote the curing.

Special version:
1.This parameter is for laboratory conditions,due to the actual working condition is more complex,suggest the users to do the pretest according to actual working condition
2.When the environment temperature is below 15℃,the curing time will prolong,should take proper heating measure
3.When the environment temperature is more than 25℃ or the mixing quantity is too large,the curing speed will expedite,should properly shorten the application time of coating after mixing.

Transportation storage
Sealed storage in the cool and dry place. The warranty period is 12 months. Avoid placing it upside down, knocking against and transporting it as a non-dangerous product during transportation.

Packaging specifications:
Two components,10Kgs/set,packed in a plastic drum.

------分隔线----------------------------